1c:I[5547,["/_next/static/chunks/89260d4cd98c65d0.js","/_next/static/chunks/ac172589c0b5f554.js","/_next/static/chunks/5bbab2bfd3ce8927.js","/_next/static/chunks/42f9cd710c2c2ebb.js","/_next/static/chunks/b12170a0ff7e7237.js","/_next/static/chunks/8cc95d0dca2cfd91.js","/_next/static/chunks/7638e934ec374cd1.js","/_next/static/chunks/3c475380227a8e03.js","/_next/static/chunks/7742c0e06bb9ba6a.js","/_next/static/chunks/9e256c93310f37c8.js","/_next/static/chunks/ac4b707d8f76f4ed.js","/_next/static/chunks/594b2291d3c465e2.js","/_next/static/chunks/82b44da47925fea9.js","/_next/static/chunks/a5e57c5c2aa9ff98.js"],"default"] 1d:T4bf,

TYPE	DATA
Item Code	NW2936
Suture material	VICRYL* Braided Polyglactin 910 Undyed
Suture Type	VICRYL*
Suture USP	3-0
Suture Length	70 CM
Usage Tissue Type	Skin
QTY/BoX	12
Absorbability	Absorbable
Sterilization Type	ETO-T.S. Cycle
Pledget	No
Suture Color	UNDYED
Suture Construction	Braided
Needle Color	Silver
Needle Length (mm)	24 MM
Needle Alloy	Ethalloy
Needle TYPE	Reverse Cutting-PS PRIME

1e:T4f4,

- Needle Length: 24mm

- Suture Length: 70cm

- Colour: Undyed

- Suture Type: Synthetic Braided

- Absorption Profile: Absorbable : 56 - 70 Days (Average 63 Days)

- Suture Diameter: USP 3-0

- Suture Material: Polyglactin 910

- Needle Description: 24mm, 3/8 Circle Reverse Cutting PS-1 Needle

- Coating: Calcium Stearate

- Tensile Strength: 75% retention at 14 days, 50% retention at 21 days, 25% retention at 28 days

- The Coated Vicryl Suture is indicated for use in general soft tissue approximation and/or ligation, including use in ophthalmic procedures, but not for use in cardiovascular or neurological tissues

- The Coated Vicryl Suture is a synthetic absorbable sterile surgical suture composed of a copolymer made from 90% glycolide and 10% L-lactide

- This suture, being absorbable, should not be used where extended approximation of tissue is required

- Progressive loss of tensile strength and eventual absorption of Coated Vicryl Suture occurs by means of hydrolysis. Absorption begins as a loss of tensile strength followed by a loss of mass.